纯PTFE强度低、耐磨性差以及耐蠕变性不好,通常要在PTFE聚合物中添加一些无机颗粒，如石墨、二硫化钼、三氧化二铝、玻纤、碳纤维等来提高其力学性能；也可利用与其他聚合物如聚苯酯(PHB)、聚苯硫醚(PPS)、聚醚醚酮(PEEK)、聚全氟（乙烯/丙烯）共聚物(PFEP)等共混的方法来扩展其阻尼温度范围，提高其耐蠕变性。 [2] 生产方法 　　聚四氟乙烯由四氟乙烯经自由基聚合而生成。工业上的聚合反应是在大量水存在下搅拌进行的，用以分散反应热，并便于控制温度。聚合一般在40～80℃，3～26千克力/厘米2压力下进行，可用无机的过硫酸盐、**过氧化物为引发剂，也可以用氧化还原引发体系。每摩尔四氟乙烯聚合时放热171.38kJ。
3M™ Dyneon™ PTFE Compound TF 2274 3M Advanced Materials Division   PTFE
3M™ Dyneon™ PTFE Compound TF 3105 3M Advanced Materials Division   PTFE
3M™ Dyneon™ PTFE Compound TF 3215 3M Advanced Materials Division   PTFE
3M™ Dyneon™ PTFE Compound TF 3310 3M Advanced Materials Division   PTFE
3M™ Dyneon™ PTFE Compound TF 3311 3M Advanced Materials Division   PTFE
3M™ Dyneon™ PTFE Compound TF 3712 3M Advanced Materials Division   PTFE
3M™ Dyneon™ PTFE Compound TF 4102 3M Advanced Materials Division   PTFE
3M™ Dyneon™ PTFE Compound TF 4103 3M Advanced Materials Division   PTFE
3M™ Dyneon™ PTFE Compound TF 4104 3M Advanced Materials Division   PTFE
3M™ Dyneon™ PTFE Compound TF 4105 3M Advanced Materials Division   PTF

⑸PTFE的导热系数低，导热性能较差，这不仅妨碍它用作轴承材料，而且使得制造厚壁制品时不能淬火。　 　　⑹PTFE的线膨胀系数为钢的10~20倍，比多数塑料大，其线膨胀系数随着温度的变化而发生很不规律的变化。在应用PTFE时，如果对这方面性能注意不够，很*造成损失。　 　　⑺在400℃以上加热时，聚四氟乙烯的裂解速度逐渐加快，分解产物主要是四氟乙烯、全氟丙烯和八氟环丁烷。在475℃ 以上，分解产物有少量剧毒的。注意加热温度不能**过400℃，且实验室要有良好的通风系统，利于排除毒性气体。

聚四氟乙烯(PTFE)使用条件行业 化工、石化、炼油、氯碱、制酸、磷肥、制药、、化纤、染化、焦化、煤气、**合成、有色冶炼、钢铁、原子能及高分子过滤材料、高纯产品生产（如离子膜电解），粘稠物料输送与操作，卫生要求高度严格的食品、饮料等加工生产部门。

3M™ Dyneon™ PTFE Compound TF 4215 3M Advanced Materials Division   PTFE
3M™ Dyneon™ PTFE Compound TF 4216 3M Advanced Materials Division   PTFE
3M™ Dyneon™ PTFE Compound TF 4302 3M Advanced Materials Division   PTFE
3M™ Dyneon™ PTFE Compound TF 4303 3M Advanced Materials Division   PTFE
3M™ Dyneon™ PTFE Compound TF 4705 3M Advanced Materials Division   PTFE
3M™ Dyneon™ PTFE Compound TF 6105-N    3M Advanced Materials Division   PTFE
3M™ Dyneon™ PTFE Compound TF 6220 3M Advanced Materials Division   PTFE
3M™ Dyneon™ PTFE Compound TF 6221 3M Advanced Materials Division   PTFE
3M™ Dyneon™ PTFE Compound TF 6302 3M Advanced Materials Division   PTFE
3M™ Dyneon™ PTFE Compound TF 6404 3M Advanced Materials Division   PTFE
3M™ Dyneon™ PTFE Compound TF 6406 3M Advanced Materials Division   PTFE
3M™ Dyneon™ PTFE Compound TF 6711 3M Advanced Materials Division   PTFE
3M™ Dyneon™ PTFE Compound TF 7149 3M Advanced Materials Division   PTFE
3M™ Dyneon™ PTFE Compound TF 7921 3M Advanced Materials Division   PTFE
预成型
要尽可能终端使用性能，就必须施加足够的预成型压力。一般压力范围为3,000到4,500 psi，停留时间因预制件尺寸不同而有所不同。在较低压力下预成型的毛坯形状其物理性能（比重，拉伸强度，拉伸率，弯曲寿命）、电气性能以及耐渗透和耐化学性比较低劣。